As the raw material of various yarn to narrow web-like fabric or tubular fabric. There are a wide range of fabric, widely used in clothing, shoe, luggage, industrial, agriculture, military, transportation and other industrial sectors. 1930s, webbing are hand workshop production, raw materials for cotton, twine. After the establishment of new China, raw material web to the progressive development of nylon, vinylon, polyester, polypropylene, polyurethane, rayon and the like, is formed of woven, knitted, knitting technology, the fabric structure has three categories plain, twill, satin, Jacquard, double, multi-layer, tubular and joint tissue.
Edit polyester webbing materials (PET):
1, strong wear.
2, poor water absorption, moisture regain 0.4% (20 ℃, relative humidity of 65%, 100g water-absorbing polyester 0.4g).
3, prone to static electricity, easy to pilling.
4, acid alkali. Note: a certain concentration of base damage soft feel of polyester fabric surface at a certain temperature.
5, corrosion resistance, light resistance is better.
6, polyester fiber woven fabric prepared not wrinkle, good dimensional stability, drying washable.
Polyester spinning:
1, FDY (filament): monofilament parallel smooth and uniform, divided into large bright, bright, semi-gloss, matte, brightness increasingly weak.
2, DTY (elastic yarn): monofilament bending, low elasticity, fluffy, as shown in FIG.
3, DTY wire network (INTERLACED wire): a stage for Network point, increased too bundling capabilities between fibers (non-network division, a light mesh, grille, net weight, wherein the weight of pulp fiber web may be free).
Under normal circumstances, FDY and DTY need for sizing before twisting or warp.
Sizing: wires have to increase strength; give cohesion between the fibers; fiber surface is smooth, easy to weaving.
Twisting: increased strength; to give cohesion between the fibers increases; the fabric has a crepe effect.
Twist: (T) units have to twist a few centimeters thread.
0-10 T / CM weak twist
10-20 T / CM in a twist
20 T / CM Jiangnian
. 4, POY (pre-oriented yarn): extensible non-resilient, do not warp or weft alone, other fiber composite must be stretched 1.6 times, POY filament yarn is obtained semifinished INTERLACED. Typical Fabric: Washed.
5, ATY (air-textured yarn): the surface is not smooth, there is a loop. Typical fabrics: cashmere Tasi
6, PSF: a plurality of axially by twisting short fibers.
7, bamboo polyester filament: filament textured yarn by twisting and, slow speed stretch yarn.
8, high-wire: high-elasticity and high loft.
9, polyester cationic yarn: it can produce with ordinary polyester yarn color effects, easily dyed, bright color.
Polyamide (PA) or nylon NYLON (N):
1, Strong is very good, even more than the same fineness wire.
2, wear resistance is very good, more than other textile fibers, suitable for sportswear, socks, parachutes, ropes.
3, poor water absorption, 4% moisture regain, easy-static, pilling, pilling.
4, not acid alkali, 37.5% hydrochloric acid is dissolved.
5, good corrosion resistance, poor water resistance, light resistance, poor heat resistance, yellowing long drying strength decreased.
6, nylon garment prepared easily deformed, easy to wrinkle.
Spinning forms: mainly FDY, ATY.
Polyurethane (PU):
Nature: 500-800 extensible%, lower strength, perspiration, water resistance, acid resistance, good alkali resistance, do not separate latitude and longitude lines, must be coated with other yarns.
Spandex covered main forms: the null packets (obviously can see spandex); Pack (Spandex is wrapped inside)
Island composite wire: mixed fiber composite wire is formed by coalescence network Haidao Si and high-shrinkage filaments.
High shrinkage yarn: a boiling water shrinkage rate of 35% (the rate was so large suede).
Haidao Si: microfiber, single fiber up to 0.138 (produce velvety suede).
Viscose (R) viscose fiber:
1, the same chemical composition and cotton, cotton performance close;
2, good moisture absorption than cotton, easily stained, dyed bright, good color fastness;
3, a low wet strength, 40-60% of dry strength, elasticity in a wet state, poor wear resistance, viscose woven fabric is not washable, poor dimensional stability.
Spinning forms: viscose filament yarn - rayon - rayon
Viscose staple fiber - rayon - people cotton
Acetate fiber acetate
1, 6% moisture regain, semi-hydrophobic fibers;
2, the strength is not good enough, silk-like luster, smooth feel;
3, soft, easy to deform, wear resistance is poor;
4, compared with the viscose, cellulose acetate low strength, poor moisture absorption, poor dyeability, feel, elasticity, gloss, superior thermal viscose fiber.
Metal filament wire
Stainless steel monofilament specifications 0.035mm-0.28mm
Function: flash, electrically conductive, flame retardant, radiation function
Taixing Hongyang New Materials Technology Co., Ltd. has consistently adhered to the "excellent quality, customer first, quality service, adhere to the contract," the purpose, with high-quality products, good reputation, selling the country. Wholeheartedly with the domestic business win-win cooperation and common development!
- International oil price flash crash 6%! Some big factories have raised the price of raw materials?
- The more prominent use of polypropylene high-strength yarn is in the industrial field
- 2024 Keqiao Fashion Week (Autumn) kicks off
- Polypropylene high strength yarn has excellent characteristics
- We will promote high-end and intelligent industries with traditional advantages
- Polypropylene high strength yarn is stronger
- China has become a world apparel producer and exporter
- What affects the tension of polypropylene high strength yarn?
- Western China (forward) textile and garment industry transfer development docking conference opened
- Polypropylene (PP) yarn woven ribbon is collectively referred to as polypropylene webbing